Property*

Unit

ASTM Method

Plasticizer

%

-

10

Flow Designation

D 569

MH

Flow Temperature

^oC

^oF

D 569

150

302

Specific Gravity

D 792

1.19

MECHANICAL

Tensile Stress @ Yield
50 mm/min (2 in./min)

MPa

psi

D 638

33.1

4,800

Tensile Stress @ Break
50 mm/min (2 in./min)

MPa

psi

D 638

43.4

6,300

Elongation @ Break
50 mm/min (2 in./min)

%

D 638

50

Flexural Modulus of Elasticity
1.27 mm/mm (0.05 in./min)

MPa

10⁵ psi

D 790

1,379

2.00

Flexural Yield Strength
1.27 mm/min (0.05 in./min)

MPa

psi

D 790

45.5

6,600

Rockwell Hardness

R Scale

D 785

78

THERMAL

PERMANENCE

Water Absorption (24h Immersion)

%

D 570

1.4

Soluble Matter Loss

%

0.1

Weight Loss on Heating [72h @ 80°C (176°F)]

%

D 707

0.5

Unless noted otherwise, all tests are run @ 23°C (73°F) and 50% relative humidity.

*Properties reported here are typical of average lots. Busada Manufacturing makes no representation that the material in any particular shipment will conform exactly to the values given.